Wood Template-Supported Phase Change Material Composites for Durable and Form-Stable Thermal Energy Storage in Buildings: Article No. 102120

To reduce and shift peak energy loads in buildings, phase change materials (PCMs) with high transition enthalpies and transition temperatures near human thermal comfort are desirable for thermal energy storage (TES). Traditional solid/liquid PCMs suffer from leakage during thermal cycling, requiring encapsulation that lowers heat storage capacity. Wood templates (WTs), with porous and hierarchical structures, provide natural encapsulation scaffolds for PCM containment. Polyethylene glycol (PEG) is a compatible PCM with WTs, but when infiltrated alone, ~30 wt% of PEG binds to wood with no detectable phase change, limiting TES efficiency. To address this, we developed a method to (1) improve the form stability of balsa and pine-based composites (BWT + PCMs and PWT + PCMs) and (2) reduce inactive PCM within the composites to ~10 wt%. BWT + PCMs exhibit transition properties upwards of 114.2 J/g at 25.4 degrees C, with no degradation after 1000 thermal cycles, and similar stiffness compared to raw balsa. Meanwhile, PWT + PCMs exhibit 25 % higher storage efficiency with the addition of poly(ethylene glycol) diacrylate compared to solely PEG-infiltrated PWT. PWT + PCM retains 84 % of raw pine's mechanical stiffness, sufficient for light-duty construction. Our shape-stabilized WT + PCM composites enrich the functionality of wood materials as both ideal TES material candidates and light-duty building construction applications.