Towards Spatial Control of Reaction Selectivity on Photocatalysts using Area Selective Atomic Layer Deposition on Model Dual Site Electrocatalyst Platform

Photocatalytic water splitting is a promising route to low-cost H2; however, this approach is currently limited by solar-to-hydrogen (STH) conversion efficiencies in the sub-10% range. Z-scheme water splitting, in which H2 and O2 evolving particles are operated in separate compartments and electronically coupled by a soluble redox mediator, offers improvements in STH efficiency but introduces high rates of undesired side and back reactions. Nanoscopic oxide coatings (e.g., CrOx, and SiOx) have previously been used to selectively block undesired reactants from reaching active sites; however, a coating encapsulating the entire photocatalyst particle limits activity as the particle can no longer facilitate both half reactions. In contrast to photodeposition, which may produce non-uniform overlayers due to the difficulty of controlling local electrochemical reactivity on the surface, area-selective atomic layer deposition (AS-ALD) can be used to deposit conformal ultrathin oxide coatings while preserving access to non-growth areas of a substrate surface. To develop this technique for Z-scheme photocatalysts, we performed AS-ALD of TiO2 on a dual site planar electrocatalyst based on interdigitated arrays of Pt and Au. Self-assembled monolayers of 1-octadecanethiol (ODT) were used to block growth on the Au array, resulting in a patterned surface in which only the Pt sites were encapsulated with TiO2. These electrocatalysts demonstrated localized reaction selectivity for hydrogen evolution reaction (HER) over the TiO2/Pt sites, while the uncoated Au sites retained activity towards Fe(II)/Fe(III) redox (FeRR). Under independent potential control, these microelectrodes showed that selectively deposited TiO2 coatings can suppress the rate of back reactions on neighboring active sites by an order of magnitude compared to uncoated control samples.