Thermal Cycling-Driven Microstructural Changes of Eutectic Al-Si Phase Change Materials in SS304 Containers Revealed by Multi-Modal Imaging: Article No. 116325

Aluminum-based Al-Si alloys are widely used as phase change materials (PCMs) in thermal energy storage (TES) systems owing to their high volumetric latent heat and superior thermal conductivity. However, their long-term reliability is limited by degradation processes that remain insufficiently understood. In this work, we employ a multimodal, correlative characterization framework to systematically resolve the degradation behavior of eutectic Al-Si PCMs in contact with SS304 containers under repeated thermal cycling. By integrating high-resolution electron microscopy, three-dimensional X-ray fluorescence (3D XRF) imaging, and differential scanning calorimetry (DSC), we directly link spatially resolved compositional and microstructural evolution to changes in thermophysical properties. The correlative analysis reveals that elemental leaching of Fe, Cr, and Ni from the stainless-steel container into the PCM drives the formation of intermetallic compounds (IMCs) both at the interface and within the bulk PCM, leading to pronounced compositional heterogeneity. These interfacial reactions and diffusion-induced transformations progressively destabilize the Al-Si eutectic, reducing the effective phase-transforming fraction. Consistent with these observations, DSC measurements show a decrease in melting temperature and latent heat of fusion with thermal cycling. These results underscore the critical influence of interfacial reactions and material compatibility on the stability, durability, and overall performance of Al-Si-based TES systems.