Strain-Driven Evolution of Structural and Carrier Recombination Dynamics in Germanium: Article No. 044063

Strain engineering in group-IV semiconductors, in particular germanium (Ge), offers a promising route for advancing next-generation optoelectronic device performance. High minority carrier lifetime serves as a direct indicator of superior material quality and device efficiency. Several factors govern the minority carrier lifetime in both strained Ge and strained GeSn, such as strain level, epilayer thickness, defects, surface roughness, and Sn alloying. In this study, the impact of biaxial strain on effective minority carrier lifetimes of tensile-strained Ge (0% ..epsilon..-Ge/Al?As, 0.78% ..epsilon..-Ge/In0.115?Ga0.885?As, and 0.93% ..epsilon..-Ge/In0.16?Ga0.84?As) and compressively strained GeSn (-0.53% c-Ge0.97?Sn0.03/Al?As) epilayers, grown by molecular beam epitaxy, was experimentally investigated via the microwave-reflection photoconductive decay (..mu..-PCD) technique as a simultaneous function of thickness and strain. The structural and strain-relaxation properties were analyzed by high-resolution x-ray diffraction and Raman spectroscopy, while surface morphology analysis using atomic force microscopy provided insights into the surface roughness of strained Ge-based epilayers. Defect characterization by cross-section transmission electron microscopy revealed superior crystalline quality of ..epsilon..-Ge in one epilayer, while twin boundary formation was observed in the other. We investigated the carrier recombination dynamics in epitaxially strained Ge by extracting the bulk recombination lifetime and surface recombination velocity using the thickness-dependent minority carrier lifetime. High effective minority carrier lifetimes of approximately 60-340 ns were achieved at high strain levels with minimal dependence on the thickness of the strained Ge-based epilayers by means of the ..mu..-PCD technique. Minority carrier lifetimes in Ge-based epilayers exhibit a quadratic dependence on the biaxial strain, ranging from -0.88% (compressive) to +1.6% (tensile). The analysis of the carrier recombination dynamics in strained Ge-based heterostructures offers a pathway to designing group-IV based optoelectronic devices.