Reducing Non-Radiative Recombination in Perovskite Solar Cells with a SiO2-Graphene Oxide Buried Interface Layer: Article No. 112209

Perovskite solar cells (PSCs) have emerged as a transformative photovoltaic technology. However, the device performance of inverted PSCs is dramatically limited by surface defects and the underlying film morphology of metal halide perovskite (MHP) thin film. Herein, we report a novel buried interface layer consisting of SiO2 nanoparticles (NPs) chemically bonded to graphene oxide (GO), deposited atop a hydrophobic hole extraction layer (HEL) to address this limitation. The SiO2 NPs serve as insoluble scaffolds that immobilize GO sheets on the hydrophobic HEL surface, enabling the formation of homogeneous MHP thin films. Meanwhile, the GO functional groups interact with surface-uncoordinated Pb2+, suppressing interfacial defects and guiding crystal grain growth of the resultant MHP thin films. This synergistic effect suppresses non-radiative charge recombination and enhances charge extraction efficiency. As a result, a 26.07% efficiency with significantly suppressed photocurrent hysteresis is observed from PSCs incorporating the SiO2-GO buried interface layer. Moreover, the above PSCs maintain 92% of their initial PCE after 1800 h of continuous operation at the maximum power point under AM 1.5 G (100 mW/cm2) illumination at 25 degrees C in air with 50-60% relative humidity. These results demonstrate that we have developed a facile and effective way to realize high-performance inverted PSCs.