Phosphonic-Acid-Reinforced Polymer Hole Transport Layers for Deployable p-i-n Perovskite Photovoltaics: Article No. 100431

The long-term durability prospects of halide perovskite solar cells are rapidly improving; however, the interface between the hole transport layer (HTL) and the perovskite remains a source of degradation. Alone, polymer- or carbazole-based HTLs suffer from incomplete coverage of the underlying indium tin oxide glass, leading to degradation and compromised performance. Here, we show a multi-HTL approach whereby a polymer HTL is reinforced using a phosphonic acid modification leading to better protection of the buried perovskite interface and more columnar growth of perovskite film, resulting in an ~40-mV open-circuit voltage (VOC) improvement indicative of suppressed interfacial recombination across multiple p-i-n device architectures. Solar cells with this reinforced HTL show higher tolerance to several accelerated stress tests. We report, among the best durabilities for unencapsulated cells, a T90 ~3,000 h (T80 ~5,900 h) at 65 degrees C under continuous 1.2 sun AM 1.5G illumination and maximum power point tracking, representing a nearly 4-fold increase compared with [2-(9H-carbazol-9-yl)ethyl]phosphonic acid (2PACz)-only devices. Furthermore, we deployed a device with this reinforced HTL on a cube satellite, with long-duration operational space testing results exceeding T80 for the complete mission duration of ~100 days in low Earth orbit.