Influence of Pt-Metal Alloy Catalysts with Various Ionomers on Oxygen Reduction Reaction in Fuel Cell Application: Article No. 121863

Pt-M/C (M = Co, Ni, Mn, etc.) alloy catalysts exhibit superior oxygen reduction reaction (ORR) activity compared to pure Pt/C, leading to a high energy efficiency in hydrogen fuel cells. However, many Pt-M/C alloy catalysts were synthesized and evaluated at the lab scale in model test-bed systems like rotating disc electrodes, which don't always correlate to performance within a fuel cell system; there is a clear need to evaluate catalysts in electrodes that can be prepared at industrially relevant scales to evaluate how factors like ink formulation can greatly affect device-level of fuel cell performance. Herein, three commercial Pt-M/C alloy catalysts (two Pt-Co/C and one Pt-Ni/C) were comprehensively characterized by various techniques. The results show that the average particle sizes of the three catalysts are close to 5 nm; the atomic ratio of Pt/M is around 4; and the M was successfully embedded into Pt lattice, resulting in the positive shift of Pt 4f in XPS spectra and XRD patterns. These catalytic materials were incorporated into 9 different cathode catalyst layers (CCLs) with three kinds of ionomers (Nafion D2020, high oxygen permeability ionomer (HOPI), and Aquivion D79-25BS), and their performance in proton exchange membrane fuel cells (PEMFCs) were investigated. The results demonstrate that the Pt-Co/C catalysts possess a higher mass activity (MA) than Pt-Ni/C; the cathodes with Nafion ionomer provide the highest MA while electrodes with Aquivion ionomer showed the lowest activity, attributed to poor H+ conductivity resulting from suboptimal ionomer incorporation. Finally, these alloys were shown to exceed DOE targets for MA and H2/Air performance reported in the recent publications at beginning of life and after 90k cycle catalyst AST protocol. This study provides valuable performance benchmarks for these materials guiding future Pt-M/C catalyst design and material integration for heavy duty PEMFC applications.